Apec? 1745
聚碳酸酯
MVR (330°C/2.16kg) 17 cm3/10 min; easy release; suitable for superheated steam sterilisation up to 143 °C as well as for pharmaceutical applications according to United States Pharmacopeia (USP) XXII Class VI; softening temperature (VST/B 120)=170 °C; injection molding - melt temperature 320 - 340°C; Films for medical packaging; Contact lens holders; Medical vessels; Safety valve for respiration aids; Syringe tops
特性 | |
用途 | - 薄膜、閥門/閥門部件、藥物醫(yī)療/護(hù)理用品、醫(yī)療器械、醫(yī)用包裝
|
機(jī)構(gòu)評(píng)級(jí) | |
RoHS 合規(guī)性 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 (73°F) | 1.17 | g/cm3 | ISO 1183 |
熔流率（熔體流動(dòng)速率） (330°C/2.16 kg) | 17 | g/10 min | ISO 1133 |
熔融體積流量（MVR） (330°C/2.16 kg) | 1.04 | in3/10min | ISO 1133 |
收縮率 3 |
|
| ISO 294-4 |
橫向流量 : 0.0787 in | 0.80 | % |
|
流量 : 0.0787 in | 0.80 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.30 | % |
|
平衡, 73°F, 50% RH | 0.12 | % |
|
球壓硬度 | 17400 | psi | ISO 2039-1 |
拉伸模量 (73°F) | 348000 | psi | ISO 527-2/1 |
拉伸應(yīng)力 (屈服, 73°F) | 10200 | psi | ISO 527-2/50 |
拉伸應(yīng)變 (屈服, 73°F) | 6.8 | % | ISO 527-2/50 |
標(biāo)稱拉伸斷裂應(yīng)變 (73°F) | > 50 | % | ISO 527-2/50 |
彎曲模量 4 (73°F) | 348000 | psi | ISO 178 |
彎曲應(yīng)力 4 (73°F) | 15200 | psi | ISO 178 |
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 |
|
| ISO 179/1eU |
-22°F | 無(wú)斷裂 |
|
|
73°F | 無(wú)斷裂 |
|
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 320 | °F | ISO 75-2/B |
264 psi, 未退火 | 298 | °F | ISO 75-2/A |
維卡軟化溫度 | 338 | °F | ISO 306/B120 |
線形熱膨脹系數(shù) |
|
| ISO 11359-2 |
流動(dòng) : 73 到 131°F | 3.6E-5 | in/in/°F |
|
橫向 : 73 到 131°F | 3.6E-5 | in/in/°F |
|
RTI Elec | 284 | °F | UL 746 |
RTI Imp | 266 | °F | UL 746 |
RTI | 284 | °F | UL 746 |
表面電阻率 | 1.0E+16 | ohms | IEC 60093 |
體積電阻率 (73°F) | 1.0E+17 | ohms·cm | IEC 60093 |
介電強(qiáng)度 (73°F, 0.0394 in) | 890 | V/mil | IEC 60243-1 |
相對(duì)電容率 |
|
| IEC 60250 |
73°F, 100 Hz | 3.00 |
|
|
73°F, 1 MHz | 2.90 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
73°F, 100 Hz | 1.0E-3 |
|
|
73°F, 1 MHz | 8.0E-3 |
|
|
漏電起痕指數(shù) |
|
| IEC 60112 |
解決方案 A | 250 | V |
|
解決方案 B | 125 | V |
|
UL 阻燃等級(jí) (0.06 in) | HB |
| UL 94 |
灼熱絲易燃指數(shù) | 1560 | °F | IEC 60695-2-12 |
極限氧指數(shù) 5 | 25 | % | ISO 4589-2 |
折射率 6 | 1.578 |
| ISO 489 |
透射率 (39.4 mil) | 88.0 | % | ISO 13468-2 |
Electrolytical Corrosion (73°F) | A1 |
| IEC 60426 |
如需科思創(chuàng)原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！