Stanyl? TW250F6
聚酰胺 46
產(chǎn)品說(shuō)明:
30% Glass Reinforced, Heat Stabilized, Flame Retardant
Special Features:
Stanyl? is our high-performance polyamide 46 used for applications in automotive, E&E, gears and outdoor power equipments.
Stanyl is a high performance polyamide that provides unmatched performance and value for demanding applications in which superior heat resistance, design stiffness, wear & friction and process flow qualities are required.
Because Stanyl retains its mechanical properties at high temperatures up to 220°C, this makes it ideal for extremely high-performance applications, where it outperforms PPA, PA6T, PA9T, and often PPS and LCP.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | Isochronous Stress vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)
|
樹(shù)脂ID (ISO 1043) | |
密度 | 1.68 | -- | g/cm3 | ISO 1183 |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 1.1 | -- | % |
|
流量 | 0.40 | -- | % |
|
吸水率 |
|
|
| ISO 62 |
飽和, 73°F | 5.9 | -- | % |
|
平衡, 73°F, 50% RH | 1.6 | -- | % |
|
粘數(shù) | 145 | -- | cm3/g | ISO 307 |
拉伸模量 |
|
|
| ISO 527-2 |
-- | 1.74E+6 | 1.16E+6 | psi |
|
248°F | 1.09E+6 | -- | psi |
|
320°F | 899000 | -- | psi |
|
拉伸應(yīng)力 |
|
|
| ISO 527-2 |
斷裂 | 26100 | 18100 | psi |
|
斷裂, 248°F | 15200 | -- | psi |
|
斷裂, 320°F | 13800 | -- | psi |
|
拉伸應(yīng)變 |
|
|
| ISO 527-2 |
斷裂 | 2.5 | 3.5 | % |
|
斷裂, 248°F | 4.0 | -- | % |
|
斷裂, 320°F | 4.0 | -- | % |
|
彎曲模量 |
|
|
| ISO 178 |
-- | 1.60E+6 | 1.06E+6 | psi |
|
248°F | 943000 | -- | psi |
|
320°F | 725000 | -- | psi |
|
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eA |
-22°F | 4.8 | 4.8 | ft·lb/in2 |
|
73°F | 5.2 | 5.2 | ft·lb/in2 |
|
簡(jiǎn)支梁無(wú)缺口沖擊強(qiáng)度 |
|
|
| ISO 179/1eU |
-22°F | 24 | 24 | ft·lb/in2 |
|
73°F | 29 | 29 | ft·lb/in2 |
|
懸壁梁缺口沖擊強(qiáng)度 |
|
|
| ISO 180/1A |
-40°F | 5.2 | 5.2 | ft·lb/in2 |
|
73°F | 5.2 | 5.2 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 554 | -- | °F | ISO 75-2/B |
264 psi, 未退火 | 554 | -- | °F | ISO 75-2/A |
玻璃轉(zhuǎn)化溫度 3 | 167 | -- | °F | ISO 11357-2 |
維卡軟化溫度 | 554 | -- | °F | ISO 306/B50 |
熔融溫度 3 | 563 | -- | °F | ISO 11357-3 |
線形熱膨脹系數(shù) |
|
|
| ISO 11359-2 |
流動(dòng) | 1.4E-5 | -- | in/in/°F |
|
橫向 | 3.1E-5 | -- | in/in/°F |
|
RTI Elec (0.030 in) | 284 | -- | °F | UL 746 |
Effective Thermal Diffusivity | 1.11E-7 | -- | m2/s |
|
Thermal Index - 5000 hr | 351 | -- | °F | IEC 60216 |
可燃性等級(jí) |
|
|
| IEC 60695-11-10, -20 |
0.030 in | V-0 | -- |
|
|
0.06 in | V-0 | -- |
|
|
極限氧指數(shù) | 37 | -- | % | ISO 4589-2 |
干燥溫度 | 176 | °F |
干燥時(shí)間 | 4.0 到 8.0 | hr |
料筒后部溫度 | 536 到 608 | °F |
料筒中部溫度 | 572 到 608 | °F |
料筒前部溫度 | 572 到 608 | °F |
射嘴溫度 | 572 到 608 | °F |
加工（熔體）溫度 | 581 到 608 | °F |
模具溫度 | 176 到 248 | °F |
注射速度 | 中等偏快 |
|
背壓 | 290 到 1450 | psi |
螺桿壓縮比 | 2.5:1.0 |
|
如需恩驊力（Envalior）原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我司工作人員，謝謝！