TECHNYL STAR? AFX 216 V60 GREY 2327
聚酰胺66
產(chǎn)品說明:
TECHNYL STAR? AFX 216 V60 Grey 2327 is a high flow polyamide 66 resin, reinforced with 60% of glass fibre, for injection moulding. Due to its outstanding flow caracteristics, this grade shows exceptional processing behaviour and excellent surface aspect of the finished part.
填料/增強(qiáng)材料 | |
特性 | - 尺寸穩(wěn)定性良好、出色的外觀、剛性，高、流動性高
|
用途 | |
機(jī)構(gòu)評級 | |
外觀 | |
形式 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | |
樹脂ID (ISO 1043) | |
密度 | 1.71 | -- | g/cm3 | ISO 1183/A |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 0.45 | -- | % |
|
流量 | 0.35 | -- | % |
|
吸水率 (73°F, 24 hr) | 0.52 | -- | % | ISO 62 |
拉伸模量 |
|
|
|
|
73°F | 2.84E+6 | -- | psi | ASTM D638 |
73°F | 3.19E+6 | 2.39E+6 | psi | ISO 527-2/1A |
抗張強(qiáng)度 |
|
|
|
|
斷裂, 73°F | 36300 | -- | psi | ASTM D638 |
斷裂, 73°F | 37700 | 28300 | psi | ISO 527-2/1A |
伸長率 |
|
|
|
|
屈服, 73°F | 2.0 | -- | % | ASTM D638 |
斷裂, 73°F | 2.0 | -- | % | ASTM D638 |
斷裂, 73°F | 2.2 | 2.9 | % | ISO 527-2 |
彎曲模量 |
|
|
|
|
73°F | 2.61E+6 | -- | psi | ASTM D790 |
73°F | 2.61E+6 | 1.91E+6 | psi | ISO 178 |
彎曲強(qiáng)度 |
|
|
|
|
73°F | 53700 | -- | psi | ASTM D790 |
73°F | 58000 | 43500 | psi | ISO 178 |
簡支梁缺口沖擊強(qiáng)度 (73°F) | 7.1 | 7.1 | ft·lb/in2 | ISO 179/1eA |
簡支梁無缺口沖擊強(qiáng)度 (73°F) | 43 | 41 | ft·lb/in2 | ISO 179/1eU |
懸壁梁缺口沖擊強(qiáng)度 (73°F) | 3.2 | -- | ft·lb/in | ASTM D256 |
載荷下熱變形溫度 |
|
|
|
|
264 psi, 未退火 | 487 | -- | °F | ASTM D648 |
264 psi, 未退火 | 496 | -- | °F | ISO 75-2/Af |
熔融溫度 | 504 | -- | °F | ISO 11357-3 |
UL 阻燃等級 |
|
|
| UL 94 |
0.031 in | HB | -- |
|
|
0.06 in | HB | -- |
|
|
0.13 in | HB | -- |
|
|
干燥溫度 | 176 | °F |
|
建議的最大水分含量 | 0.20 | % |
|
料筒后部溫度 | 509 到 527 | °F |
|
料筒中部溫度 | 518 到 536 | °F |
|
料筒前部溫度 | 536 到 554 | °F |
|
模具溫度 | 140 到 194 | °F |
|
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4h Injection Advice: For reinforced polyamides, Solvay recommends the use of steel with a high content of carbon, and purified for polishing, to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). In the case of high requirements on surface quality a mould temperature of up to 120°C can be considered.
|
如需索爾維（SOLVAY）原廠物性表及相關(guān)文件，請聯(lián)系我們工作人員，謝謝！