TECHNYL? A 218 V15 BLACK 51
聚酰胺66
產(chǎn)品說明:
TECHNYL? A 218 V15 Black 51 is a polyamide 66, reinforced with 15% of glass fibre, heat stabilized, for injection moulding. This grade offers an excellent combination between thermal and mechanical properties.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | - Heat Stabilized - Inorganic，尺寸穩(wěn)定性良好，良好的流動性，脫模性能良好
|
用途 | - 電氣/電子應(yīng)用領(lǐng)域，工業(yè)應(yīng)用，連接器，消費(fèi)品應(yīng)用領(lǐng)域
|
機(jī)構(gòu)評級 | |
RoHS 合規(guī)性 | |
外觀 | |
形式 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | |
樹脂ID (ISO 1043) | |
密度 | 1.24 | -- | g/cm3 | ISO 1183/A |
收縮率 |
|
|
| ISO 294-4 |
橫向流量 | 1.4 | -- | % |
|
流量 | 0.50 | -- | % |
|
吸水率 (73°F, 24 hr) | 1.1 | -- | % | ISO 62 |
拉伸模量 (73°F) | 899000 | 624000 | psi | ISO 527-2/1A |
拉伸應(yīng)力 (斷裂, 73°F) | 18100 | 13100 | psi | ISO 527-2/1A |
拉伸應(yīng)變 (斷裂, 73°F) | 4.0 | -- | % | ISO 527-2 |
彎曲模量 (73°F) | 769000 | 508000 | psi | ISO 178 |
彎曲應(yīng)力 (73°F) | -- | 16700 | psi | ISO 178 |
簡支梁缺口沖擊強(qiáng)度 (73°F) | 2.9 | 4.8 | ft·lb/in2 | ISO 179/1eA |
簡支梁無缺口沖擊強(qiáng)度 (73°F) | 21 | 38 | ft·lb/in2 | ISO 179/1eU |
懸壁梁缺口沖擊強(qiáng)度 (73°F) | 4.8 | 6.2 | ft·lb/in2 | ISO 180/1A |
無缺口伊佐德沖擊強(qiáng)度 (73°F) | 19 | 33 | ft·lb/in2 | ISO 180/1U |
載荷下熱變形溫度 |
|
|
|
|
66 psi, 未退火 | 428 | -- | °F | ASTM D648 |
264 psi, 未退火 | 473 | -- | °F | ISO 75-2/Af |
熔融溫度 | 505 | -- | °F | ISO 11357-3 |
表面電阻率 | 6.0E+15 | 1.0E+13 | ohms | IEC 60093 |
體積電阻率 | 1.0E+15 | 1.0E+15 | ohms·cm | IEC 60093 |
介電強(qiáng)度 (0.0787 in) | 790 | 760 | V/mil | IEC 60243-1 |
耗散因數(shù) | 0.010 | 0.11 |
| IEC 60250 |
漏電起痕指數(shù) (解決方案 A) | 450 | 325 | V | IEC 60112 |
UL 阻燃等級 (0.13 in) | HB | -- |
| UL 94 |
極限氧指數(shù) | 24 | -- | % | ISO 4589-2 |
干燥溫度 | 176 | °F |
|
建議的最大水分含量 | 0.20 | % |
|
料筒后部溫度 | 518 到 536 | °F |
|
料筒中部溫度 | 527 到 545 | °F |
|
料筒前部溫度 | 536 到 554 | °F |
|
模具溫度 | 158 到 212 | °F |
|
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4h Injection Advice: For reinforced polyamides, Solvay recommends the use of steel with a high content of carbon, and purified for polishing, to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). In the case of high requirements on surface quality a mould temperature of up to 120°C can be considered.
|