TORZEN Marathon? G3500XHL BK34
聚酰胺66
PA66 35% glass fiber reinforced injection molding grade with enhanced thermal resistance in contact with hot air. High improvement of mechanical properties retention versus standard polyamide 66 after heat ageing. Black colour.
Suitable for parts requiring high stiffness, good mechanical resistance and good heat ageing properties retention.
填料/增強(qiáng)材料 | |
特性 | - Good Heat Resistance、剛性高、良好的耐熱老化性能
|
RoHS 合規(guī)性 | |
外觀 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.42 | g/cm3 | ISO 1183 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.90 到 1.1 | % |
|
流量 | 0.25 到 0.35 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F, 0.0787 in | 1.1 | % |
|
平衡, 73°F, 0.0787 in, 50% RH | 1.7 | % |
|
拉伸模量 | 1.67E+6 | psi | ISO 527-2/1A/1 |
拉伸應(yīng)力 (斷裂) | 30500 | psi | ISO 527-2/1A/5 |
拉伸應(yīng)變 (斷裂) | 3.0 | % | ISO 527-2/1A/5 |
彎曲模量 2 | 1.52E+6 | psi | ISO 178 |
彎曲應(yīng)力 2 | 46400 | psi | ISO 178 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179/1eA |
-40°F | 4.8 | ft·lb/in2 |
|
73°F | 5.7 | ft·lb/in2 |
|
懸壁梁缺口沖擊強(qiáng)度 (73°F) | 5.7 | ft·lb/in2 | ISO 180/1A |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 500 | °F | ISO 75-2/Bf |
264 psi, 未退火 | 482 | °F | ISO 75-2/Af |
熔融溫度 3 | 504 | °F | ISO 11357-3 |
干燥溫度 - 熱風(fēng)干燥機(jī) | 176 | °F |
|
干燥時(shí)間 - 熱風(fēng)干燥機(jī) | 2.0 到 4.0 | hr |
|
Dew Point - 熱風(fēng)干燥機(jī) | -4 | °F |
|
建議的最大水分含量 | 0.15 | % |
|
加工（熔體）溫度 | 536 到 572 | °F |
|
模具溫度 | 176 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
如需蘭蒂奇原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！