Desmopan? 9648DU
熱塑性聚氨酯彈性體（聚醚）
Extrusion- and injection molding grade; with special UV stabilizers; transparent up to 6 mm wall thickness; very good hydrolysis and microbial resistance; Application; Ski boot shells; Hoses, non-reinforced
添加劑 | |
特性 | |
用途 | |
RoHS 合規(guī)性 | |
加工方法 | |
密度 (73°F) | 1.16 | g/cm3 | ISO 1183 |
肖氏硬度 |
|
| ISO 7619 |
邵氏 A, 1 秒, 73°F | 94 |
|
|
邵氏 D, 1 秒, 73°F | 48 |
|
|
拉伸應力 2 |
|
| DIN 53504 |
斷裂, 73°F | 7510 | psi |
|
10% 應變, 73°F | 740 | psi |
|
50% 應變, 73°F | 1700 | psi |
|
100% 應變, 73°F | 2290 | psi |
|
300% 應變, 73°F | 4610 | psi |
|
拉伸應變 2 (斷裂, 73°F) | 430 | % | DIN 53504 |
彎曲模量 3 (73°F) | 8700 | psi | ISO 178 |
Tensile Storage Modulus |
|
| ISO 6721 |
-4°F | 125 | ksi |
|
68°F | 19.3 | ksi |
|
140°F | 7.54 | ksi |
|
抗磨損性 4 | 20.0 | mm3 | ISO 4649 |
撕裂強度 5 (73°F) | 650 | lbf/in | ISO 34-1 |
壓縮永久變形 |
|
| ISO 815 |
73°F, 72 hr | 38 | % |
|
158°F, 24 hr 4 | 45 | % |
|
158°F, 24 hr 6 | 27 | % |
|
Rebound Resilience | 33 | % | ISO 4662 |
干燥溫度 | < 230 | °F |
|
加工（熔體）溫度 | 419 到 455 | °F |
|
模具溫度 | 104 到 140 | °F |
|
干燥溫度 | < 230 | °F |
|
熔體溫度 | 392 到 455 | °F |
|