Arnite? TM4 440
聚對苯二甲酸丁二酯 + PET
產(chǎn)品說明:
20% Mineral Reinforced
Special Features:
Used In:
Arnite? (PBT, PET and blends) are high-performance engineering plastics that combine high strength and rigidity with excellent processing characteristics. As a result, Arnite? A (PET) and Arnite? T (PBT) are well suited for a broad range of automotive, electrical & electronic and consumer goods applications.
A wide portfolio of Arnite? is available including unreinforced, reinforced and flame retardant grades.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.48 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (270°C/2.16 kg) | 2.07 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 1.7 | % |
|
流量 | 1.4 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.35 | % |
|
平衡, 73°F, 50% RH | 0.15 | % |
|
拉伸模量 | 740000 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 8270 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 1.9 | % | ISO 527-2 |
簡支梁缺口沖擊強(qiáng)度 (73°F) | 0.86 | ft·lb/in2 | ISO 179/1eA |
簡支梁無缺口沖擊強(qiáng)度 (73°F) | 15 | ft·lb/in2 | ISO 179/1eU |
熱變形溫度 |
|
|
|
66 psi, 未退火 | 383 | °F | ISO 75-2/B |
264 psi, 未退火 | 212 | °F | ISO 75-2/A |
熔融溫度 2 | 437 | °F | ISO 11357-3 |
可燃性等級 (0.06 in) | HB |
| IEC 60695-11-10, -20 |
干燥溫度 | 212 到 248 | °F |
|
干燥時(shí)間 | 3.0 到 12 | hr |
|
料筒后部溫度 | 464 | °F |
|
料筒中部溫度 | 464 到 482 | °F |
|
料筒前部溫度 | 482 到 500 | °F |
|
射嘴溫度 | 482 到 500 | °F |
|
加工（熔體）溫度 | 500 到 518 | °F |
|
模具溫度 | 140 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 435 到 1450 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|
如需恩驊力（Envalior）原廠物性表及相關(guān)文件，請聯(lián)系我司工作人員，謝謝！