Arnite? TV4 251 XG2 (T-X07602)
聚丁烯對(duì)苯二甲酸酯
產(chǎn)品說明:
25% Glass Reinforced, Flame Retardant (halogen free)
Special Features:
Used In:
Arnite? (PBT, PET and blends) are high-performance engineering plastics that combine high strength and rigidity with excellent processing characteristics. As a result, Arnite? A (PET) and Arnite? T (PBT) are well suited for a broad range of automotive, electrical & electronic and consumer goods applications.
A wide portfolio of Arnite? is available including unreinforced, reinforced and flame retardant grades.
填料/增強(qiáng)材料 | |
添加劑 | |
特性 | |
用途 | |
加工方法 | |
樹脂ID (ISO 1043) | |
密度 | 1.54 | g/cm3 | ISO 1183 |
熔融體積流量（MVR） (250°C/2.16 kg) | 1.10 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 1.3 | % |
|
流量 | 0.70 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 0.30 | % |
|
平衡, 73°F, 50% RH | 0.15 | % |
|
拉伸模量 | 1.23E+6 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂) | 13800 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂) | 2.0 | % | ISO 527-2 |
簡支梁缺口沖擊強(qiáng)度 |
|
| ISO 179/1eA |
-22°F | 2.4 | ft·lb/in2 |
|
73°F | 2.4 | ft·lb/in2 |
|
簡支梁無缺口沖擊強(qiáng)度 |
|
| ISO 179/1eU |
-22°F | 14 | ft·lb/in2 |
|
73°F | 14 | ft·lb/in2 |
|
熱變形溫度 |
|
|
|
66 psi, 未退火 | 428 | °F | ISO 75-2/B |
264 psi, 未退火 | 410 | °F | ISO 75-2/A |
熔融溫度 2 | 437 | °F | ISO 11357-3 |
漏電起痕指數(shù) | 550 | V | IEC 60112 |
可燃性等級(jí) (0.030 in) | V-2 |
| IEC 60695-11-10, -20 |
灼熱絲易燃指數(shù) |
|
| IEC 60695-2-12 |
0.030 in | 1760 | °F |
|
0.06 in | 1760 | °F |
|
干燥溫度 | 212 到 248 | °F |
|
干燥時(shí)間 | 3.0 到 6.0 | hr |
|
料筒后部溫度 | 446 到 464 | °F |
|
料筒中部溫度 | 455 到 482 | °F |
|
料筒前部溫度 | 464 到 491 | °F |
|
射嘴溫度 | 464 到 500 | °F |
|
加工（熔體）溫度 | 464 到 500 | °F |
|
模具溫度 | 140 到 212 | °F |
|
注射速度 | 中等偏快 |
|
|
背壓 | 435 到 1450 | psi |
|
螺桿壓縮比 | 2.5:1.0 |
|
|