Ultrason? E 2010 G4
聚醚砜
產(chǎn)品說明:
Ultrason E 2010 G4 is a 20% glass reinforced, medium viscosity injection molding PESU grade with high rigidity and strength.
Applications
Typical applications include circuit braker parts, lamp holders, heat shields, impellers, and printer cartridges.
填料/增強(qiáng)材料 | |
特性 | |
用途 | |
機(jī)構(gòu)評(píng)級(jí) | |
RoHS 合規(guī)性 | |
形式 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Specific Volume vs Temperature (ISO 11403-2) Viscosity vs. Shear Rate (ISO 11403-2)
|
密度 | 1.50 | g/cm3 | ISO 1183 |
溶化體積流率（MVR） (360°C/10.0 kg) | 1.77 | in3/10min | ISO 1133 |
收縮率 |
|
| ISO 294-4 |
橫向流量 | 0.61 | % |
|
流量 | 0.36 | % |
|
吸水率 |
|
| ISO 62 |
飽和, 73°F | 1.6 | % |
|
平衡, 73°F, 50% RH | 0.60 | % |
|
球壓硬度 | 29700 | psi | ISO 2039-1 |
拉伸模量 (73°F) | 1.00E+6 | psi | ISO 527-2 |
拉伸應(yīng)力 (斷裂, 73°F) | 18900 | psi | ISO 527-2 |
拉伸應(yīng)變 (斷裂, 73°F) | 3.2 | % | ISO 527-2 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 |
|
| ISO 179 |
-22°F | 3.8 | ft·lb/in2 |
|
73°F | 3.8 | ft·lb/in2 |
|
簡(jiǎn)支梁無缺口沖擊強(qiáng)度 |
|
| ISO 179 |
-22°F | 31 | ft·lb/in2 |
|
73°F | 29 | ft·lb/in2 |
|
懸壁梁缺口沖擊強(qiáng)度 |
|
| ISO 180 |
-22°F | 3.8 | ft·lb/in2 |
|
73°F | 3.8 | ft·lb/in2 |
|
熱變形溫度 (264 psi, 未退火) | 432 | °F | ISO 75-2/A |
線形熱膨脹系數(shù) - 流動(dòng) | 1.1E-5 | in/in/°F |
|
RTI Elec |
|
| UL 746 |
0.06 in | 356 | °F |
|
0.12 in | 356 | °F |
|
RTI Imp |
|
| UL 746 |
0.06 in | 356 | °F |
|
0.12 in | 356 | °F |
|
RTI |
|
| UL 746 |
0.06 in | 374 | °F |
|
0.12 in | 374 | °F |
|
表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
介電強(qiáng)度 | 940 | V/mil | IEC 60243-1 |
介電常數(shù) |
|
| IEC 60250 |
100 Hz | 4.20 |
|
|
1 MHz | 4.20 |
|
|
耗散因數(shù) |
|
| IEC 60250 |
100 Hz | 2.0E-3 |
|
|
1 MHz | 0.010 |
|
|
漏電起痕指數(shù) | 125 | V | IEC 60112 |
UL 阻燃等級(jí) |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.12 in | V-0 |
|
|
干燥溫度 | 266 到 302 | °F |
|
干燥時(shí)間 | 4.0 | hr |
|
建議的最大水分含量 | 0.020 | % |
|
加工（熔體）溫度 | 662 到 734 | °F |
|
模具溫度 | 302 到 374 | °F |
|
注塑壓力 | 508 到 1810 | psi |
|
注射速度 | 快速 |
|
|
如需巴斯夫原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！