CYCOLAC? Resin FR15
丙烯腈丁二烯苯乙烯
產(chǎn)品說明:
Flame retardant ABS (non-PBBE additive). Good property/toughness. Excellent moldability. UL94 V-0/5VA rated.
添加劑 | |
特性 | |
加工方法 | |
多點(diǎn)數(shù)據(jù) | Coefficient of Thermal Expansion vs. Temperature (ASTM E831) Flexural DMA (ASTM D4065) Shear DMA (ASTM D4065) Specific Heat vs. Temperature (ASTM D3417) Tensile Fatigue Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530) Viscosity vs. Shear Rate (ASTM D3835)
|
密度 / 比重 |
|
|
|
-- | 1.20 |
| ASTM D792 |
-- | 1.19 | g/cm3 | ISO 1183 |
熔流率（熔體流動(dòng)速率） |
|
|
|
230°C/3.8 kg | 4.0 | g/10 min | ASTM D1238 |
220°C/5.0 kg | 10 | g/10 min | ISO 1133 |
收縮率 - 流動(dòng) (0.126 in) | 5.0E-3 到 7.0E-3 | in/in | 內(nèi)部方法 |
拉伸模量 3 | 340000 | psi | ASTM D638 |
抗張強(qiáng)度 |
|
|
|
屈服 4 | 6000 | psi | ASTM D638 |
屈服 | 5980 | psi | ISO 527-2/50 |
斷裂 4 | 5100 | psi | ASTM D638 |
斷裂 | 4540 | psi | ISO 527-2/50 |
伸長(zhǎng)率 |
|
|
|
屈服 4 | 2.3 | % | ASTM D638 |
屈服 | 2.1 | % | ISO 527-2/50 |
斷裂 4 | 9.0 | % | ASTM D638 |
斷裂 | 34 | % | ISO 527-2/50 |
彎曲模量 5 (1.97 in 跨距) | 395000 | psi | ASTM D790 |
彎曲強(qiáng)度 5 (屈服, 1.97 in 跨距) | 10400 | psi | ASTM D790 |
簡(jiǎn)支梁缺口沖擊強(qiáng)度 6 (73°F) | 9.3 | ft·lb/in2 | ISO 179/1eA |
懸壁梁缺口沖擊強(qiáng)度 |
|
|
|
73°F | 4.0 | ft·lb/in | ASTM D256 |
-22°F 7 | 3.1 | ft·lb/in2 | ISO 180/1A |
73°F 7 | 8.9 | ft·lb/in2 | ISO 180/1A |
裝有測(cè)量?jī)x表的落鏢沖擊 (73°F, Total Energy) | 300 | in·lb | ASTM D3763 |
載荷下熱變形溫度 |
|
|
|
66 psi, 未退火, 0.126 in | 180 | °F | ASTM D648 |
264 psi, 未退火, 0.126 in | 158 | °F | ASTM D648 |
264 psi, 未退火, 2.52 in 跨距 8 | 164 | °F | ISO 75-2/Af |
維卡軟化溫度 |
|
|
|
-- | 187 | °F | ASTM D1525 9 |
-- | 178 | °F | ISO 306/B50 |
-- | 183 | °F | ISO 306/B120 |
線形熱膨脹系數(shù) |
|
| ASTM E831 |
流動(dòng) : -40 到 104°F | 4.7E-5 | in/in/°F |
|
橫向 : -40 到 104°F | 4.8E-5 | in/in/°F |
|
RTI Elec | 140 | °F | UL 746 |
RTI Imp | 140 | °F | UL 746 |
RTI | 140 | °F | UL 746 |
耐電弧性 10 | PLC 7 |
| ASTM D495 |
相比耐漏電起痕指數(shù)(CTI) | PLC 2 |
| UL 746 |
高電弧燃燒指數(shù)(HAI) | PLC 4 |
| UL 746 |
高電壓電弧起痕速率 (HVTR) | PLC 4 |
| UL 746 |
熱絲引燃 (HWI) | PLC 3 |
| UL 746 |
UL 阻燃等級(jí) |
|
| UL 94 |
0.06 in | V-0 |
|
|
0.10 in | 5VA |
|
|
熔體粘度 (392°F, 1000 sec^-1) | 290 | Pa·s | ASTM D3835 |
干燥溫度 | 180 到 190 | °F |
|
干燥時(shí)間 | 2.0 到 4.0 | hr |
|
干燥時(shí)間，最大 | 6.0 | hr |
|
建議的最大水分含量 | 0.10 | % |
|
建議注射量 | 50 到 70 | % |
|
料筒后部溫度 | 340 到 360 | °F |
|
料筒中部溫度 | 380 到 400 | °F |
|
料筒前部溫度 | 390 到 420 | °F |
|
射嘴溫度 | 390 到 430 | °F |
|
加工（熔體）溫度 | 390 到 430 | °F |
|
模具溫度 | 120 到 160 | °F |
|
背壓 | 50.0 到 100 | psi |
|
螺桿轉(zhuǎn)速 | 30 到 60 | rpm |
|
排氣孔深度 | 1.5E-3 到 2.0E-3 | in |
|
如需沙伯基礎(chǔ)（SABIC）原廠物性表及相關(guān)文件，請(qǐng)聯(lián)系我們工作人員，謝謝！